Solution-processed metal nanowire mesh transparent electrode for large-area electronics
Stanford Reference:
07-135
Abstract
A team of Stanford engineers have developed a low-cost, solution-processed method to fabricate a flexible nanowire mesh that can be used in transparent electrodes, as a replacement for metal oxides (such as ITO, indium tin oxide). This fabrication technique is carried out at moderate temperatures which are gentler to the underlying layers than sputtering. In addition, the resulting films are more conductive than ITO for the same transparency, resulting in solar cells that outperform devices based on ITO. Other applications for the nanowire mesh include large area electronics such as flat panel displays and light-emitting devices.
Applications
Transparent electrodes
(ITO replacement) for:
solar cells
flat panel displays
light emitting devices
Advantages
Flexible material
- nanowire mesh is not brittle and can be used on flexible substrates without cracking
High performance
- more transparent for a given sheet resistance, which leads to better devices
Low cost process
- solution casting and a moderate temperature (200
o
C) anneal
Gentle
- this process causes less damage to underlying active organic layers compared to sputtering of ITO
Publications
J.-Y. Lee, S.T. Connor, Y. Cui, P. Peumans,
"Solution-processed metal nanowire mesh transparent electrodes"
,
Nanoletters
2008.
Innovators & Portfolio
Steve Connor
Yi Cui
more technologies from Yi Cui »
Jung-Yong Lee
Peter Peumans
Patent Status
Published Application: 20100178417
Published Application: 20130098436
Issued : 8,323,744 (USA)
Issued : 9,254,505 (USA)
Date Released
2/1/2010 12:00
Licensing Contact
Jon Gortat, Licensing & Strategic Alliances Director for Physical Science
312.413.1643
Request Info
03-235
Thermal Interface Materials
04-112
High Q Inductor
04-132
A Method for Heteroepitaxial Growth of Germanium on Silicon
more technologies »
Related Keywords
PS: clean energy: photovoltaic
ITO replacement
PS: electronics: flexible
PS: hardware: flat panel displays
PS: thin film: electrodes
PS: electronics: LED (light emitting diodes)
PS: clean energy: thin film photovoltaic
PS: thin film
materials